Material:Metal,Aluminum,Anodized Aluminum,Brass,Stainless Steel,Polycarbonate,Polyester,Vinyl.
What metal plate production process
Signs, metal plate production process have?????????Signs, nameplates use in various areas of modern society, more and more widely used in electronic products, home appliances, machinery and consumer products, and other fields. Their production process in general, what does? this
Aiming at these questions on the meaning of various metal signs and metal plate production process to make a brief analysis of the metal plate so that we have a better understanding.????????Metal plate mainly in copper, iron, aluminum, zinc alloy, pewter and other raw materials for the foundation, by stamping, casting, etching, printing, enamel, imitation enamel, paint and other craft, making ChengMing
Cards, badges, badge, medals, key ring, badge, cap clip, wallet, medals, coins, craft signs, cufflinks, photo frames, mobile phone strap, tie clips, belt, tag, bottle opener and other workers
Art jewelry and a variety of metal plate, a metal plate and several different categories of various metal plate products.????????Common metal plate production mainly metal flat sun signs, metal printing plate, metal corrosion signs, metal plating and metal electroforming nameplate, metal signs and metal sandblasting thermal transfer label.
Epoxy signs manual
Epoxy plate manual operation is different from Epoxy plate machining (For more see "Epoxy signage Operating Procedures"), to distinguish between specific request from for comparison.1, the first ready for all kinds of substrates, such as: nameplates, badges, medals, etc. into the oven preheating temperature requirement of 60 degrees, the purpose of the removal of surface moisture.2, the substrate was placed flat dehumidified consistent level of console board waiting drip.3. The amount, take a clean beaker, accurate measurement, the B component, a 2: 1 weight ratio of mixing evenly (must be mixed, otherwise there will be sticky and with the substrate surface
Delamination phenomenon, the manufacturers of the products are the same to do this. ) (Note: the proportion of the manufacturers are not the same, as the case may be).4, and then with a good mixture into a vacuum oven, open real pump, removing bubbles mix in a vacuum.5, take in the clean needle, the needle after defoaming Shuijingjiao suction tube, then measure and drip evenly in the prepared substrate (ie: signs, trademarks, etc.) of the surface, the general Shuijingjiao
Thickness 2mm, let the natural leveling can be (Note: The above process is controlled within 30 minutes, so as not to increase the liquid viscosity, resulting in inoperable).6, the substrate 3-5 minutes after instillation Shuijingjiao observe glue surface without bubbles or dust particles, if any small bubbles, usable pin to pierce, found dead have not stream Shuijingjiao to place, with pin lead
Crossing can be.7, pouring good signs, at room temperature 20 ℃ -30 ℃ cured 10-24 hours harden, becoming left the surface of the crystal plate.8, in case of stickers, trademarks, etc., in itself is very thin, and the boundary is not obvious, when pouring, likely to cause Shuijingjiao spill to reach 2mm thickness will be difficult, so make Shuijingjiao grasp different situations
China [CN] 
Click enlarge Image